Acrylstyrene anticorrosive

Acrylstyrene anticorrosive priming

24.3-32388851-001-2004

Description of the priming: Single-component priming on basis acrylstyrene copolymers with the active anticorrosive pigments and the converter of rust, the plasticizer.
Field of application: Priming coating for structural and galvanized steel, aluminum. It adapts in the region of general building, mining industry, coating of supports (masts), etc.
Properties: Simplicity in the use, rapid drying, of good impregnating properties with the manual removal rusts. Possibility of putting at a temperature of air from -100 С to + 300 from the relative humidity to 85%.
Colour: red-brown, gray.
Methods of putting: brush, roller, air - airless dispersion.
Acrylstyrene priming relates to the group on the propagation of flame RP1
(it does not extend flame)
Acrylstyrene priming relates to the group on the flash V1
The form of delivery: priming is supplied by ready to application.

General technical characteris

The exterior view of the film

Uniform lusterless coating without the stratification, the foreign inclusions, the craters is formed after drying

The relative viscosity

100-250

Mass fraction of non-volatile substances, %

55 - 65

Degree of grinding, mkm

The adhesion of film marks, not more

Strength with the impact, on the instrument of the type
The u-1, sm, not less

Resistance of film to the action
waters, h, with (20+2) 0C not less

Resistance of film to action by 3% of solution NaCl, h

The resistance of film to the action of mineral oil, h, not less

Time of drying at a temperature of 20 0C and relative humidities 85%, h
To degree of 1
To degree of 3
Time of the final polymerization
At a temperature it is below against 0C

30-40 min
2 hours
72 hours
are hour about 6

Expenditure (theory)

With the thickness of dry layer 60 mkm approximately - 160 g on 1 mkm 2

Theoretical thickness of the dry film
with 1 layer

60 mkm is possible tuning from 40 mkm to 80 mkm