DH-klesch

"DH-klesch"

Acrylstyrene organic dilutable chemically resistant paint "DH - klesch"

24.3-32388851-005-2004

Description of the paint: Single-component paint on basis acrylstyrene copolymers of plasticizer, anticorrosive pigments, barrier fillers. Depending on the operating conditions of coating, modified by polybutadiene, copolymer of vinyl chloride.
Field of application: Universal coating for the protection of metal from the action of the acids of alkalis, mineral and motor oil, benzastoykoye. Depending on the surface condition of metal and operating conditions the paint "DH-klesch" adapts both the independent coating and over the preliminarily grounded surface.
Properties: simplicity in the use rapid drying. Possibility of putting at a temperature of air from -100C to +300C and relative humidity to 85%.
Colour: on the demand of customer.
The form of delivery: paint is supplied by ready to application.
Methods of putting: brush, roller, air and airless dispersion.
"DH - klesch" relates to the group on the propagation of flame RP1 (it does not extend flame)
"DH - klesch" relates to the group on the flash V1

General technical characteristics

The exterior view of the film	Uniform lusterless coating without the stratification, the foreign inclusions is formed after drying
Paint density	Approximately 1,23 - 1,40 g/sm 3V of dependence on the colour.
The relative viscosity of material on VZ-4 with t(20,0 ± 0,5) C	100-250
Mass fraction of non-volatile substances, %	54-66
The adhesion of film marks, not more	1
Elasticity with bend, mm, not more	1
Degree of grinding, mkm, not more	35
Time of drying at a temperature of 20 0C and relative humidities 85%, h To degree of 1 To degree of 3 The time is final of the polymerization At a temperature it is below against 0C	30 min 2 hours 72 hours 6 it is hour
Luster of film on the photoelectric glossimeter BF-2	Lusterless
Thickness of the dry layer	60 mkm is possible tuning from 40 to 100 mkm
Expenditure (theory)	With the thickness of dry layer - 40 mkm approximately - 112 g on 1 mkm 2 With the thickness of dry layer - 60 mkm approximately - 165 g on 1 mkm 2
Resistance to the action of water, not less	72 hours
Resistance to action by 3% of solution NaCl	48 hours
Resistance to industrial oils	48 hours
Temperature of the operation of the coating	- 30 0C to 180°C