“DH-kora”
Acryl-styrene organic dilutable paint for structural and galvanized steel “DH-kora”
24.3-32388851-005-2004
Description of the paint: Single-component paint on the basis of acrylstyrene copolymers and plasticizer.
Field of application: Universal coating for structural and galvanized steel. It is used in the systems of anticorrosive protection for painting of industrial equipment, metal structures, capacities for GSM, bridges, supports LEP, gas-, air conduits, hangars, the metallic zinc-coated roofs, which are subjected to direct environmental effect.
Properties: simplicity in the use, rapid drying, the stability of the color
Colour: on the demand of the customer
The form of delivery: paint is supplied by ready to the application
Method of putting: brush, roller, the air- airless dispersion
General technical characteristics
|
The exterior view of the film
|
Uniform coating without the stratification, the foreign inclusions is formed after drying
|
|
Paint density
|
Approximately 1,25 - 1,35 g/sm 3 depending on the colour
|
|
The relative viscosity of material on VZ-236
with t (20,0 ± 0,5) of ºC
|
100-250
|
|
Mass fraction of non-volatile substances, %
|
47-68
|
|
The adhesion of film marks, not more
|
1
|
|
Elasticity with bend, mm is not more
|
1
|
|
The strength of film with impact, sm, not less
|
50
|
|
Degree of grinding, mkm, not more
|
30
|
|
Time of drying at a temperature of 20 0 C and relative humidities 85%, h
To degree of 1
To degree of 3
Time of the final polymerization
At a temperature it is below against 0 C
|
30 min
1,5 hours
72 hours
3 hours
|
|
Luster of film on the photoelectric glossimeter BF -2
|
middlegloss, gloss, lusterless coating
|
|
Resistance to the action of water, h, not less
|
72
|
|
Resistance to industrial oils, h, not less
|
48
|
|
Resistance to 3% solution Na Cl, h, not less
|
48
|
|
Temperature of the operation of coating, °C
|
from - 30 to +180
|
|
Expenditure (theoretical)
|
With the thickness of dry layer - 40 mkm -
Approximately 106 g to 1m 2
With the thickness of dry layer 60 mkm -
Approximately 158 g to 1m 2
|
Thickness of one dry layer
|
60 m
is possible tuning from 40 to 100 mkm
|